Properties/Materials	Alumina Ceramic 95%  Pythagoras C610 ~ C795
Bulk Density (g/cm3)	3.6
Apparent Porosity (%)	≤ 0.2
Flexural Strength  at 20oC (Mpa)	250
Thermal Shock Resistance at 1,200oC	Good
Thermal Expansion at 20 ~ 1,000oC ( x 10 -6/oC )	6.2~7.5
Thermal Conductivity W/(m.K)	25
Maximum Working Temperature	1,400oC ~ 1,500oC

\п глинозема керамический 99.5% Alsint\C799 н

Properties/Materials	Alumina Ceramic 99.5%  Alsint C799
Bulk Density (g/cm3)	3.7
Apparent Porosity (%)	≤ 0.2
Flexural Strength  at 20oC (Mpa)	300
Thermal Shock Resistance at 1,200oC	Good
Thermal Expansion at 20 ~ 1,000oC ( x 10 -6/oC )	7.8~8.6
Thermal Conductivity W/(m.K)	29.2
Maximum Working Temperature	1,500oC ~ 1,700oC

\н Сыщиц (HALSIC-я) реакционно-связанного карбида кремния\п

Properties/Materials	SiSiC (HALSIC-I) Reaction-bonded Silicon Carbide
Bulk Density (g/cm3)	3.01
Apparent Porosity (%)	≤0.1
Flexural Strength  at 20oC (Mpa)	260
Thermal Shock Resistance at 1,200oC	Excellent
Thermal Expansion at 20 ~ 1,000oC ( x 10 -6/oC )	4.5
Thermal Conductivity W/(m.K)	45
Maximum Working Temperature	1,380oC

\н Наск гонки si3n4 облигационного карбида кремния sic\п

Properties/Materials	NSiC  Si3N4 Bond SiC Silicon Carbide
Bulk Density (g/cm3)	2.75~2.85
Apparent Porosity (%)	≤ 11
Flexural Strength  at 20oC (Mpa)	170~180
Thermal Shock Resistance at 1,200oC	Excellent
Thermal Expansion at 20 ~ 1,000oC ( x 10 -6/oC )	4.7
Thermal Conductivity W/(m.K)	20
Maximum Working Temperature	1,500oC

\н ВГИК (HALSIC-Р) Recristalyzed карбид кремния\н

Properties/Materials	RSiC (HALSIC-R) Recristalyzed Silicon Carbide
Bulk Density (g/cm3)	2.65~2.75
Apparent Porosity (%)	≤ 15
Flexural Strength  at 20oC (Mpa)	90~100
Thermal Shock Resistance at 1,200oC	Good
Thermal Expansion at 20 ~ 1,000oC ( x 10 -6/oC )	4.69
Thermal Conductivity W/(m.K)	36.6
Maximum Working Temperature	1,650oC

\н Чугун и обычная эмаль\п

Properties/Materials

Cast Iron  Plain and Enamel

Cast Iron Thermocouple Protection Tubes Cast iron tubes are designed to provide excellent physical strength for demanding environments including aluminium and zinc melting furnaces,the charging of scrap and ingot, as well as other applications requiring physical strength. Its design creates a robust and durable option for temperature measurement. Advantages *Enamel coating provides for good oxidation resistance *Excellent durability *Longer life from increased thickness